Processing of Nb-containing TiAl intermetallics and its Physical and Chemical Aspects
Barták, Tomáš ; Dlouhý, Ivo (oponent) ; Zemčík, Ladislav (oponent) ; Dlouhý, Antonín (vedoucí práce)
Presented study investigates vacuum induction re-melting of Ti-46Al-7Nb (at%) intermetallic alloy in refractory crucible based on Y2O3. A series of re-melting experiments was performed at melting temperatures 1630, 1680 and 1730 C and three ranges of melting times (5, 15 and 30 minutes). Metallographic cross-sections for each experiment were prepared to obtain the data of microstructure and phase composition evaluation using SEM and EDS. A quantitative assessment of microstructure was based on an Adaptive Contrast Control (ACC) software used to estimate a volume fraction of ceramic phase in the melt. Oxygen content in the solidified met was analyzed using Inert Gas Fusion (IGF) method. Thermodynamic calculations of possible reactions are presented regarding the activity of the individual elements of intermetallic and refractory crucible. Data presented in this work based on experimental results and thermodynamic calculation could be used like guide for further melting and optimization of the TiAlNb melting process.
|
|
|
Výroba a vlastnosti žáruvzdorných slitin
Majchrák, Aleš ; Myška, Martin (oponent) ; Záděra, Antonín (vedoucí práce)
Tato bakalářská práce pojednává o žáruvzdorných slitinách, konkrétně o superslitinách a vysoce entropických slitinách. V teoretické části je provedeno rozdělení těchto slitin na základě chemického složení, popis jejich vlastností, struktury a použití. Praktická část se zabývá kobaltovou slitinou UmCo50. Mezi cíle této části patří popis metalurgie dané slitiny, ověření závislosti oduhličení na době vakuování, pozorování mikrostruktury a její zhodnocení.
|
|
|
Výroba a vlastnosti žáruvzdorných slitin
Majchrák, Aleš ; Myška, Martin (oponent) ; Záděra, Antonín (vedoucí práce)
Tato bakalářská práce pojednává o žáruvzdorných slitinách, konkrétně o superslitinách a vysoce entropických slitinách. V teoretické části je provedeno rozdělení těchto slitin na základě chemického složení, popis jejich vlastností, struktury a použití. Praktická část se zabývá kobaltovou slitinou UmCo50. Mezi cíle této části patří popis metalurgie dané slitiny, ověření závislosti oduhličení na době vakuování, pozorování mikrostruktury a její zhodnocení.
|
|
|
Processing of Nb-containing TiAl intermetallics and its Physical and Chemical Aspects
Barták, Tomáš ; Dlouhý, Ivo (oponent) ; Zemčík, Ladislav (oponent) ; Dlouhý, Antonín (vedoucí práce)
Presented study investigates vacuum induction re-melting of Ti-46Al-7Nb (at%) intermetallic alloy in refractory crucible based on Y2O3. A series of re-melting experiments was performed at melting temperatures 1630, 1680 and 1730 C and three ranges of melting times (5, 15 and 30 minutes). Metallographic cross-sections for each experiment were prepared to obtain the data of microstructure and phase composition evaluation using SEM and EDS. A quantitative assessment of microstructure was based on an Adaptive Contrast Control (ACC) software used to estimate a volume fraction of ceramic phase in the melt. Oxygen content in the solidified met was analyzed using Inert Gas Fusion (IGF) method. Thermodynamic calculations of possible reactions are presented regarding the activity of the individual elements of intermetallic and refractory crucible. Data presented in this work based on experimental results and thermodynamic calculation could be used like guide for further melting and optimization of the TiAlNb melting process.
|
|
|
Interakce mezi Ti-Al-Nb taveninou a Y2O3 kelímky
Barták, Tomáš ; Dlouhý, Antonín ; Dočekalová, Kateřina ; Zemčík, L.
Příspěvek je věnován studiu interakcí mezi taveninou intermetalické slitiny Ti-46Al-7Nb-0.7Cr-0.1Si-0.2Ni (at %) a keramickými tavicími kelímky na bázi Y2O3. Pozornost je věnována vlivu taveniny na strukturu a fázové složení stěny keramických kelímků při tavbách s různou dobou výdrže na tavicí teplotě. Vakuového indukční tavby (VIM) byly provedeny ve vakuové peci BALZERS VSG 02 pod ochrannou atmosférou argonu při tlaku 0,133 bar. Studium se zaměřilo primárně na rozhraní tavenina – tavicí kelímek a bylo prováděno metodou analytické elektronové mikroskopie pomocí skenovacího elektronového mikroskopu (SEM) s energiově disperzním rentgenovým analyzátorem EDX. Výsledky dosažené v rámci této práce naznačují, že dlouhodobé expozice nad 30 min a pravděpodobně i přehřátí taveniny nad teplotu 1650°C vedou k reakcím na rozhraní Y2O3 kelímek - TiAl tavenina. Práce diskutuje stabilitu keramického systému, popisuje jednotlivá reakční rozhraní.
|
|
|
Interakce TiAl taveniny s povlakovanými keramickými tavícími kelímky
Dočekalová, Kateřina ; Dlouhý, Antonín ; Zemčík, L. ; Fiala, J.
Práce se zabývá studiem interakcí taveniny TiAl a oxidovou keramikou s povlaky. Tavby se uskutečnily ve vakuové indukční peci (VIM). Pozornost je věnována zejména mikrostruktuře odlitků a studiu interakcí na rozhraní tavenina-stěna keramického kelímku. Analýzy jsou prováděny pomocí skenovací elektronové mikroskopie (SEM) a charakteristického RTG záření metodou EDAX. K identifikaci keramických fází byla rovněž využita metoda RTG difrakce. Experimentální výsledky byly doplněny termodynamickými výpočty, zaměřenými na rovnovážné stavy chemických reakcí. Výsledky prokázaly pozitivní vliv povlaků keramické stěny tavicího kelímku na kvalitu odlitků. Práce diskutuje stabilitu povlaků, popisuje jednotlivá reakční rozhraní a pomocí kvantitativní analýzy termodynamické rovnováhy reakcí na rozhraní tavenina-kelímek vysvětluje reakční mechanismus.
|